BISPLATE 400 Wear Resistance Steel Sheet
BISPLATE 400 is a through hardened, abrasion resistant steel plate , offering long life expectancy in high impact abrasion applications.
Application:
BISPLATE 400 offers excellent wear and abrasion resistant and impact toughness in applications which include:
- Dump Truck Wear Liners
- Screw Conveyors
- Chutes
- Storage Bins
- Earth Moving Buckets
- Cyclones
- Deflector Plates
- Ground Engaging Tools
- Cutting Edges
Fabrication:
BISPLATE 400 is high hardness, abrasion resistant steel offering very good impact toughness properties.
BISPLATE 400 provides an optimum combination of abrasion resistant, toughness and weldability. Due to its
low alloy content, BISPLATE 400 can be readily welded using conventional welding processes and low hydrogen
consumables.
Cold forming of BISPLATE 400 is achievable on all thicknesses although an allowance for the higher strength should be taken into account. Bending machine capabilities should also be taken into consideration prior to any forming operation. Heating above 250ºC should be avoided, otherwise mechanical properties may be affected.
Technical:
Mechanical Properties
(Tips: You can touch and scroll right or left to see whole table on phone screen)
Properties | Specification | Typical |
|---|---|---|
0.2% Proof Stress | - | 1070 MPa |
Tensile Strength | - | 1320 MPa |
Elongation in 50mm G.L. | - | 14% |
Charpy Impact (Longitudinal) | - | 40 J |
Hardness | 370 - 430 HB | 400 HB |
Chemical Composition
| Thickness(mm) | Weight% | C | P | Mn | Si | S | Cr | Mo | B | CE (IIW)* | CET* |
|---|---|---|---|---|---|---|---|---|---|---|---|
| ≥5 - <8 | Maximum | 0.18 | 0.025 | 1.2 | 0.25 | 0.008 | 0.25 | 0.25 | 0.002 | 0.40 | 0.29 |
| ≥8 - <30 | Maximum | 0.18 | 0.025 | 1.0 | 0.60 | 0.008 | 1.00 | 0.25 | 0.002 | 0.44 | 0.26 |
| ≥30 - 80 | Maximum | 0.18 | 0.025 | 1.3 | 0.60 | 0.008 | 1.00 | 0.25 | 0.002 | 0.54 | 0.32 |
| >80 - 100 | Maximum | 0.18 | 0.025 | 1.5 | 0.60 | 0.008 | 1.20 | 0.25 | 0.002 | 0.58 | 0.34 |